Effect of solidification cooling rate on the fatigue life of A356.2-T6 cast aluminium alloy

Keyphrases

• Fatigue Life 100%
• Solidification Cooling Rate 100%
• Cast Aluminum Alloy 100%
• A356 100%
• Fatigue Crack 75%
• Cooling Rate 75%
• Ingot 50%
• Slow Cooling Rate 25%
• Stress-strain 25%
• Axial Loading 25%
• Low Cycle Fatigue 25%
• Strain Ratio 25%
• Secondary Dendrite Arm Spacing 25%
• High Cycle Fatigue 25%
• Microconstituents 25%
• Low Duty Cycle 25%
• Oxide Inclusion 25%
• Reciprocating Bending 25%
• High Cycle Fatigue Test 25%
• Bending Condition 25%

Engineering

• Cooling Rate 100%
• Fatigue Life 100%
• Fatigue Crack 50%
• High Cycle Fatigue 33%
• Mechanical Fatigue Test 16%
• Axial Loading 16%
• Critical Size 16%
• Eutectics 16%
• Slow Cooling 16%
• Arm Spacing 16%
• Low Cycle Fatigue 16%
• Oxide Inclusion 16%